ausblenden:
Schlagwörter:
Gallium;
Oxide;
Porosity;
Polymorphism
Zusammenfassung:
α, β and γ-Ga₂O₃ have been successfully obtained in an easily scalable synthesis using aqueous solution of gallium nitrate and sodium carbonate as starting materials without any surfactant and additive. α and β-Ga₂O₃ were obtained by calcination at 350 and 700 °С, respectively, of α-GaOOH, prepared by controlled precipitation at constant pH 6 and T = 55 °С, with 24 h of aging. Aging was necessary to fully convert the initially preciptated gel into a well-crystalline and phase-pure material. γ-Ga₂O₃ was obtained after calcination at 500 °С of gallia gel, synthesized at constant pH 4 and T = 25 °С, without aging. These three polymorphs have a for gallia relatively high surface area: 55 m²/g (α-Ga₂O₃), 23 m²/g (β-Ga₂O₃) and 116 m²/g (γ-Ga₂O₃). The combination of X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX), nitrogen physisorption and thermogravimetry (TG) was employed to characterize the samples and their formation.