  Charging and discharging behavior of solvothermal LiFePO4 cathode material investigated by combined EELS/NEXAFS study

Schuster, M. E., Teschner, D., Popovic, J., Ohmer, N., Girgsdies, F., Tornow, J., et al. (2014). Charging and discharging behavior of solvothermal LiFePO4 cathode material investigated by combined EELS/NEXAFS study. Chemistry of Materials, 26(2), 1040-1047. doi:10.1021/cm403115t.

Item is

 

einblenden: alle ausblenden: alle

Basisdaten

einblenden: ausblenden:
Datensatz-Permalink: https://hdl.handle.net/11858/00-001M-0000-0018-070F-1 Versions-Permalink: https://hdl.handle.net/21.11116/0000-0007-D7C1-C
Genre: Zeitschriftenartikel

Dateien

einblenden: Dateien
ausblenden: Dateien
:
1896598.pdf (Verlagsversion), 4MB
 
Datei-Permalink:
-
Name:
1896598.pdf
Beschreibung:
-
OA-Status:
Sichtbarkeit:
Eingeschränkt (Max Planck Institute of Colloids and Interfaces, MTKG; )
MIME-Typ / Prüfsumme:
application/pdf
Technische Metadaten:
Copyright Datum:
-
Copyright Info:
-
Lizenz:
-

Externe Referenzen

einblenden:

Urheber

einblenden:
ausblenden:
 Urheber:
Schuster, Manfred Erwin, Autor
Teschner, Detre, Autor
Popovic, Jelena, Autor
Ohmer, Nils, Autor
Girgsdies, Frank, Autor
Tornow, Julian, Autor
Willinger, Marc Georg, Autor
Samuelis, Dominik, Autor
Titirici, M. M.1, Autor           
Maier, Joachim, Autor
Schlögl, Robert, Autor
Affiliations:
1Kolloidchemie, Max Planck Institute of Colloids and Interfaces, Max Planck Society, ou_1863288              

Inhalt

einblenden:
ausblenden:
Schlagwörter: -
 Zusammenfassung: LiFePO4 cathode material obtained via solvothermal
synthesis was investigated at several charging and discharging stages by a
combination of bulk (EELS) and surface sensitive (NEXAFS) methods in
order to get insight into the distribution of Li in the surface and bulk region
of the particles. Different behavior was observed as a function of the
particles morphology. The turbostratic stacking of layers in nanosized
crystals induces higher dimensional defects responsible for sluggish Li
insertion and extraction within the structure. In contrast, microstructured
crystals without higher dimensional defects do not exhibit sluggish Li
insertion/extraction, and achieve a higher degree of reversibility during
electrochemical cycling.

Details

einblenden:
ausblenden:
Sprache(n): eng - English
 Datum: 2013-12-112013-09-182013-12-192013-12-192014
 Publikationsstatus: Erschienen
 Seiten: 8
 Ort, Verlag, Ausgabe: -
 Inhaltsverzeichnis: -
 Art der Begutachtung: Expertenbegutachtung
 Identifikatoren: DOI: 10.1021/cm403115t
 Art des Abschluß: -

Veranstaltung

einblenden:

Entscheidung

einblenden:

Projektinformation

einblenden:

Quelle 1

einblenden:
ausblenden:
Titel: Chemistry of Materials
  Andere : Chem. Mater.
Genre der Quelle: Zeitschrift
 Urheber:
Affiliations:
Ort, Verlag, Ausgabe: Washington, D.C. : American Chemical Society
Seiten: - Band / Heft: 26 (2) Artikelnummer: - Start- / Endseite: 1040 - 1047 Identifikator: ISSN: 0897-4756