Zusammenfassung:
We have succeeded in growing epitaxial films of rocksalt VOx on MgO(001) substrates. The oxygen content as a function of oxygen flux was determined using O-18(2)-Rutherford backscattering spectrometry and the vanadium valence using x-ray-absorption spectroscopy. The upper and lower stoichiometry limits found are similar to those known for bulk material (0.8<x<1.3). From the reflection high-energy electron diffraction oscillation period a large number of vacancies for both vanadium and oxygen were deduced, i.e., approximate to16% for stoichiometric VO. These numbers are, surprisingly, very similar to those for bulk material and consequently quite strain insensitive. X-ray-absorption spectroscopy measurements reveal that the vacancies give rise to strong non-cubic crystal field effects. The electrical conductivity of the films is much lower than the conductivity of bulk samples, which we attribute to a decrease in the direct overlap between t(2g) orbitals in the coherently strained layers. The temperature dependence of the conductivity is consistent with a variable range hopping mechanism.