  Mechanokatalytische CO-PROX

Eckert, R. (2017). Mechanokatalytische CO-PROX. PhD Thesis, Ruhr-Universität, Bochum.

Item is

Basisdaten

einblenden: ausblenden:
Genre: Hochschulschrift

Externe Referenzen

einblenden:

Urheber

einblenden:
ausblenden:
 Urheber:
Eckert, Rene1, Autor           
Affiliations:
1Research Department Schüth, Max-Planck-Institut für Kohlenforschung, Max Planck Society, ou_1445589              

Inhalt

einblenden:
ausblenden:
Schlagwörter: -
 Zusammenfassung: In the field of heterogeneous catalysis, the concept of mechanocatalysis – i.e. the application of mechanical force during a catalytic reaction – remains almost unexplored. In this work, the continuous preferential oxidation of CO in an excess of H2 (CO-PROX) was carried out by means of mechanocatalysis. By in-situ ball milling of metal oxides or copper / metal oxide mixtures, an increase in the CO oxidation rate by several orders of magnitude was achieved. Over mixtures of Cu powder with Cr2O3, considerable CO oxidation activity
was achieved at temperatures as low
as -40 °C, while undesired side reactions,
such as H2 oxidation,
were largely suppressed. During ball milling, the CO oxidation rate was up to 4 orders of magnitude higher than over the pre-milled catalyst in a conventional flow reactor. At low temperatures < 70 °C, both CO conversion and CO2 selectivity increased with decreasing temperature, corresponding to an apparent activation energy EA≈ -4 kJ mol-1. Due to the high selectivity
in the ball mill compared to flow reactor experiments, the drastic increase in
activity during milling can not be explained by thermal effects alone. Instead, we postulate that during milling, CO oxidation takes place selectively on mechanically induced, short-lived active sites. With the assumption that these active sites are surface defects, a simple kinetic model was proposed to explain the negative EA. According to this model, the slower healing rate of defects at low temperatures results in a higher defect concentration. Thus, a negative EA can be expected if the temperature dependence of the defect healing rate is greater than that of the CO oxidation rate. The drastic and highly selective, mechanically induced enhancement of a particular reaction in comparison to undesired side reactions is a novel discovery which highlights the potential of mechanocatalysis in the field of heterogeneous catalysis.
As a side project, highly active nano-Au/TiO2 catalysts were prepared by ball milling of Au powder and
commercial TiO2 under reaction conditions. The activity of these catalysts with regards to CO-PROX
was comparable to benchmark Au/TiO2 catalysts which
were prepared by conventional methods such as deposition precipitation. This novel “top down” approach of preparing supported nano-Au catalysts by ball milling
has several key advantages. Most
importantly, the preparation is carried out in a single step without the need for Au(III) precursors or solvents.

Details

einblenden:
ausblenden:
Sprache(n): deu - German
 Datum: 2017-03-312017-03-31
 Publikationsstatus: Erschienen
 Seiten: 158
 Ort, Verlag, Ausgabe: Bochum : Ruhr-Universität
 Inhaltsverzeichnis: -
 Art der Begutachtung: -
 Identifikatoren: URN: urn:nbn:de:hbz:294-52465
 Art des Abschluß: Doktorarbeit

Veranstaltung

einblenden:

Entscheidung

einblenden:

Projektinformation

einblenden:

Quelle

einblenden: