We have investigated the crystal and magnetic structure of Mn 2 PtPd alloy using powder x-ray and neutron diffraction experiments. This compound is believed to belong to the Heusler family having crystal symmetry I 4/ mmm (TiAl 3 -type). However, in this work we found that the Pd and Pt atoms are disordered and thus Mn 2 PtPd crystallizes in the L 1 0 structure having P 4/ mmm symmetry (CuAu-I type) like MnPt and MnPd binary alloys. The lattice constants are a = 2.86 Å and c = 3.62 Å at room temperature. Mn 2 PtPd has a collinear antiferromagnetic spin structure below the Néel temperature T N = 866 K, where Mn moments of ~4 µ B lie in the ab -plane. We observed a strong change in the lattice parameters near T N . The sample exhibits metallic behaviour, where electrical resistivity and carrier concentration are of the order of 10 −5 Ω cm and 10 21 cm −3 , respectively.