Abstract:
The direct evolution of submonolayer two-dimensional Au phases on the Si(111)-(7x7) surface was studied in real time using the spectroscopic photoemission and low energy electron microscope located at the synchrotron radiation source ELETTRA. A finite area covered by 1 monolayer (ML) of gold with a steplike
transition zone was prepared by evaporation in situ. Subsequent annealing resulted in the spread of the Au layer and the formation of laterally extended Si(111)-(5x1)-Au and Si(111)-(√3x √3)R30°-Au surface reconstructions. At a temperature around 970 K, the boundary of the gold-covered region propagates on the clean Si(111)-(7x7) and exhibits a nonlinear dependence on time. The ordered Si(111)-(5x1)-Au plateau develops a separated front moving with constant velocity. Two values of the Au diffusion coefficients were estimated at a temperature of about 985 K: (1) D7x7=5,2x10-8 cm2 s-1 as the average diffusion coefficient for Au on a clean Si(111)-(7x7) surface in the concentration range from 0.4 ML up to 0.66 ML and (2) D5x1=1.2x10-7 cm2 s-1 as the lower limit for the diffusion of single Au atoms on the Si(111)-(5x1)-Au ordered phase.