Chromium alloys; Chromium steel; Manganese alloys; Manganese steel; Martensite; Needles; Ternary alloys; Vanadium alloys, Damascus steel; Habit plane; Mis-orientation, Vanadium steel
Zusammenfassung:
A martensite needle was extracted from 90MnCrV8 steel (1150 °C/air) and marked. To examine the structure and the mechanical properties on that needle with habit plane, misorientation measurements and subsequent nanoindentation were performed. © Carl Hanser Verlag GmbH Co. KG.