Zusammenfassung:
Metal-organic frameworks (MOFs) provide exceptional chemical tunability and have recently been demonstrated to exhibit electrical conductivity and related functional electronic properties. The kagomé lattice is a fruitful source of novel physical states of matter, including the quantum spin liquid (in insulators) and Dirac fermions (in metals). Small-bandgap kagomé materials have the potential to bridge quantum spin liquid states and exhibit phenomena such as superconductivity but remain exceptionally rare. Here we report a structural, thermodynamic, and transport study of the two-dimensional kagomé metal-organic frameworks Ni3(HIB)2 and Cu3(HIB)2 (HIB = hexaiminobenzene). Magnetization measurements yield Curie constants of 0.989 emu K (mol Ni)-1 Oe-1 and 0.371 emu K (mol Cu)-1 Oe-1, respectively, close to the values expected for ideal S = 1 Ni2+ and S = 1/2 Cu2+. Weiss temperatures of -10.6 and -14.3 K indicate net weak mean field antiferromagnetic interactions between ions. Electrical transport measurements reveal that both materials are semiconducting, with gaps (Eg) of 22.2 and 103 meV, respectively. Specific heat measurements reveal a large T-linear contribution γof 148(4) mJ mol-fu-1 K-2 in Ni3(HIB)2 with only a gradual upturn below 5 K and no evidence of a phase transition to an ordered state down to 0.1 K. Cu3(HIB)2 also lacks evidence of a phase transition above 0.1 K, with a substantial, field-dependent, magnetic contribution below 5 K. Despite them being superficially in agreement with the expectations of magnetic frustration and spin liquid physics, we ascribe these observations to the stacking faults found from a detailed analysis of synchrotron X-ray diffraction data. At the same time, our results demonstrate that these MOFs exhibit localized magnetism with simultaneous proximity to a metallic state, thus opening up opportunities to explore the connection between the insulating and metallic ground states of kagomé materials in a highly tunable chemical platform. © 2022 American Chemical Society.