  On the CO-Oxidation over Oxygenated Ruthenium

Rosenthal, D., Girgsdies, F., Timpe, O., Blume, R., Weinberg, G., Teschner, D., et al. (2009). On the CO-Oxidation over Oxygenated Ruthenium. Zeitschrift für Physikalische Chemie, 223(1-2), 183-207. doi:10.1524/zpch.2009.6032.

Item is

Basisdaten

einblenden: ausblenden:
Genre: Zeitschriftenartikel

Dateien

einblenden: Dateien
ausblenden: Dateien
:
404116Rosenthal.pdf (Preprint), 2MB
Name:
404116Rosenthal.pdf
Beschreibung:
-
OA-Status:
Sichtbarkeit:
Öffentlich
MIME-Typ / Prüfsumme:
application/pdf / [MD5]
Technische Metadaten:
Copyright Datum:
-
Copyright Info:
-
Lizenz:
-
:
736327CTA.pdf (Verlagsvertrag), 2MB
 
Datei-Permalink:
-
Name:
736327CTA.pdf
Beschreibung:
-
OA-Status:
Sichtbarkeit:
Privat
MIME-Typ / Prüfsumme:
application/pdf
Technische Metadaten:
Copyright Datum:
-
Copyright Info:
-
Lizenz:
-
:
736327.pdf (Korrespondenz), 612KB
 
Datei-Permalink:
-
Name:
736327.pdf
Beschreibung:
-
OA-Status:
Sichtbarkeit:
Privat
MIME-Typ / Prüfsumme:
application/pdf
Technische Metadaten:
Copyright Datum:
-
Copyright Info:
-
Lizenz:
-

Externe Referenzen

einblenden:

Urheber

einblenden:
ausblenden:
 Urheber:
Rosenthal, Dirk1, Autor           
Girgsdies, Frank1, Autor           
Timpe, Olaf1, Autor           
Blume, Raoul1, Autor           
Weinberg, Gisela1, Autor           
Teschner, Detre1, Autor           
Schlögl, Robert1, Autor           
Affiliations:
1Inorganic Chemistry, Fritz Haber Institute, Max Planck Society, ou_24023              

Inhalt

einblenden:
ausblenden:
Schlagwörter: Ruthenium; CO-Oxidation; In-situ XRD; Oscillations Ruthenium in Catalysis
 Zusammenfassung: The oxidation of carbon monoxide over polycrystalline ruthenium dioxide (RuO2) powder was studied in a packed-bed reactor and by bulk and surface analytical methods. Activity data were correlated with bulk phases in an in-situ X-ray diffraction (XRD) setup at atmospheric pressure. Ruthenium dioxide was pre-calcined in pure oxygen at 1073 K. At this stage RuO2 is completely inactive in the oxidation of CO. After a long induction period in the feed at 503 K RuO2 becomes active with 100% conversion, while in-situ XRD reveals no changes in the RuO2 diffraction pattern. At this stage selective roughening of apical RuO2 facets was observed by scanning electron microscopy (SEM). Seldom also single lateral facets are roughened. EDX indicated higher oxygen content in the following order: flat lateral facets > rough lateral facets > rough apical facets. Further, experiments in the packed bed reactor indicated oscillations in the CO2 formation rate. At even higher temperatures in reducing feed (533–543 K) the sample reduces to ruthenium metal according to XRD. The reduced particles exhibiting lower ignition temperature are very rough with cracks and deep star-shaped holes. An Arrhenius plot of the CO2 formation rate below the ignition temperature reveals the reduced samples to be significantly more active based on mass unit and shows lower apparent activation energy than the activated oxidized sample. Micro-spot X-ray photoelectron spectroscopy (XPS) and XPS microscopy experiments were carried out on a Ru(0001) single crystal exposed to oxygen at different temperature. Although low energy electron diffraction (LEED) images show a strong 1×1 pattern, the XPS data indicated a wide lateral inhomogeneity with different degree of oxygen dissolved in the subsurface layers. All these and the literature data are discussed in the context of different active states and transport issues, and the metastable nature of a phase mixture under conditions of high catalytic activity.

Details

einblenden:
ausblenden:
Sprache(n): eng - English
 Datum: 2009-02
 Publikationsstatus: Erschienen
 Seiten: -
 Ort, Verlag, Ausgabe: -
 Inhaltsverzeichnis: -
 Art der Begutachtung: Expertenbegutachtung
 Identifikatoren: eDoc: 404116
DOI: 10.1524/zpch.2009.6032
 Art des Abschluß: -

Veranstaltung

einblenden:

Entscheidung

einblenden:

Projektinformation

einblenden:

Quelle 1

einblenden:
ausblenden:
Titel: Zeitschrift für Physikalische Chemie
  Alternativer Titel : Z. Phys. Chem.
Genre der Quelle: Zeitschrift
 Urheber:
Affiliations:
Ort, Verlag, Ausgabe: -
Seiten: - Band / Heft: 223 (1-2) Artikelnummer: - Start- / Endseite: 183 - 207 Identifikator: ISSN: 0942-9352