In situ observation of dislocation nucleation and escape in a submicrometre aluminium single crystal

MPS-Authors
There are no MPG-Authors in the publication available
External Resource
No external resources are shared
Fulltext (public)
There are no public fulltexts stored in PuRe
Supplementary Material (public)
There is no public supplementary material available
Citation

Oh, S. H., Legros, M., Kiener, D., & Dehm, G. (2009). In situ observation of dislocation nucleation and escape in a submicrometre aluminium single crystal. Nature Materials, 8(2), 95-100. doi:10.1038/NMAT2370.


Cite as: http://hdl.handle.net/11858/00-001M-0000-0024-55DA-5
Abstract
‘Smaller is stronger’ does not hold true only for nanocrystalline materials1 but also for single crystals2–5. It is argued that this effect is caused by geometrical constraints on the nucleation and motion of dislocations in submicrometre-sized crystals6,7. Here, we report the first in situ transmission electron microscopy tensile tests of a submicrometre aluminium single crystal that are capable of providing direct insight into sourcecontrolled dislocation plasticity in a submicrometre crystal. Single-ended sources emit dislocations that escape the crystal before being able to multiply. As dislocation nucleation and loss rates are counterbalanced at about 0.2 events per second, the dislocation density remains statistically constant throughout the deformation at strain rates of about 10-4 s-1. However, a sudden increase in strain rate to 10-3 s-1 causes a noticeable surge in dislocation density as the nucleation rate outweighs the loss rate. This observation indicates that the deformation of submicrometre crystals is strain-rate sensitive.