Magnetism and structural chemistry of ternary gallides RENixGa4−x(RE=; La, Ce, Pr, Nd, Sm, Gd, Tb) and LaCo0.5Ga3.5

MPG-Autoren
Es sind keine MPG-Autoren in der Publikation vorhanden
Externe Ressourcen
Es sind keine externen Ressourcen hinterlegt
Volltexte (beschränkter Zugriff)
Für Ihren IP-Bereich sind aktuell keine Volltexte freigegeben.
Volltexte (frei zugänglich)
Es sind keine frei zugänglichen Volltexte in PuRe verfügbar
Ergänzendes Material (frei zugänglich)
Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar
Zitation

Grin, Y. N., Hiebl, K., & Rogl, P. (1990). Magnetism and structural chemistry of ternary gallides RENixGa4−x(RE=; La, Ce, Pr, Nd, Sm, Gd, Tb) and LaCo0.5Ga3.5. Journal of the Less Common Metals, 162(2), 361-369. doi:10.1016/0022-5088(90)90351-J.


Zitierlink: https://hdl.handle.net/11858/00-001M-0000-0019-875A-C
Zusammenfassung
Ternary gallides with the chemical formula (La, Ce, Pr, Nd, Sm, Gd, Tb) NixGa4 − x, (Ce, Pr, Nd, Sm)NiGa3 and LaCo0.5Ga3.5 have been synthesized from the elements by arc melting. From X-ray powder diffraction analysis the RENixGa4−x compounds and LaCo0.5Ga3.5 were found to be isostructural and to adopt the BaAl4-type structure. The homogeneous range at 600 °C for the CeNixGa4 − x phase has been established revealing a remarkable positive deviation from Vegard's rule. The existence of new ternary compounds RENiGa3 with the CePtGa3 type was observed for RE ; Ce, Pr, Nd, and Sm at the stoichiometric composition which, however, is found within the region of the BaAl4-type structure. Magnetic susceptibilities were determined over a temperature range from 2 to 900 K. Above LNT, magnetic behaviour of the rare earth compounds (except lanthanum and samarium) of both structural series is characterized by the paramagnetic contribution of the tripositive rare earth free-ion moments. LaNi0.75Ga3.25 and LaCo0.5Ga3.5 are weakly paramagnetic. Samarium-containing alloys are characterized by a typical Van Vleck-type paramagnetism of closely spaced multiplets. At very low temperatures (T<20 K) for the ceric-nickel-gallides ferromagnetism is encountered, whereas for (Sm, Gd, Tb)NixGa4 − x the coupling of the 4f moments is antiparallel.