Insights into the structural, electronic, and magnetic properties of Fe2-xTixO3
/Fe2O3 thin films with x=0.44 grown on Al2O3 (0001)

Dennenwaldt, Teresa; Lübbe, Maike; Winklhofer, Michael; Müller, Alexander; Döblinger, Markus; Nabi, Hasan Sadat; Gandman, Maria; Cohen-Hyams, Tzipi; Kaplan, Wayne D.; Moritz, Wolfgang; Pentcheva, Rossitza; Scheu, Christina

doi:10.1007/s10853-014-8572-x

Item

ITEM ACTIONSEXPORT

Add to Basket

Local TagsRelease HistoryDetailsSummary

Released

Journal Article

Insights into the structural, electronic, and magnetic properties of Fe_2-xTi_xO₃/Fe₂O₃ thin films with x=0.44 grown on Al₂O₃ (0001)

MPS-Authors

There are no MPG-Authors in the publication available

External Resource

No external resources are shared

Fulltext (restricted access)

There are currently no full texts shared for your IP range.

Fulltext (public)

There are no public fulltexts stored in PuRe

Supplementary Material (public)

There is no public supplementary material available

Citation

Dennenwaldt, T., Lübbe, M., Winklhofer, M., Müller, A., Döblinger, M., Nabi, H. S., et al. (2015). Insights into the structural, electronic, and magnetic properties of Fe_2-xTi_xO₃/Fe₂O₃ thin films with x=0.44 grown on Al₂O₃ (0001). Journal of Materials Science, 50(1), 122-137. doi:10.1007/s10853-014-8572-x.

Cite as: https://hdl.handle.net/11858/00-001M-0000-0024-B73D-0

Abstract

The interface between hematite (alpha-(Fe2O3)-O-III) and ilmenite ((FeTiO3)-Ti-II), a weak ferrimagnet and an antiferromagnet, respectively, has been suggested to be strongly ferrimagnetic due to the formation of a mixed valence layer of Fe2+/Fe3+ (1: 1 ratio) caused by compensation of charge mismatch at the chemically abrupt boundary. Here, we report for the first time direct experimental evidence for a chemically distinct layer emerging at heterointerfaces in the hematite-Ti-doped-hematite system. Using molecular beam epitaxy, we have grown thin films (similar to 25 nm thickness) of alpha-Fe2O3 on alpha-Al2O3 (0001) substrates, which were capped with a similar to 25 nm thick Fe2-xTixO3 layer (x = 0.44). An additional 3 nm cap of alpha-Fe2O3 was deposited on top. The films were structurally characterized in situ with surface X-ray diffraction, which showed a partial low index orientation relationship between film and substrate in terms of the [0001] axis and revealed two predominant domains with (0001)(Fe2O3) vertical bar vertical bar (0001)(Al2O3,) one with [10 (1) over bar0](Fe2O3) vertical bar vertical bar [10 (1) over bar0](Al2O3), and a twin domain with [01 (1) over bar0](Fe2O3) vertical bar vertical bar [10 (1) over bar0]Al2O3. Electron energy loss spectroscopy profiles across the Fe2-xTixO3/Fe2O3 interface show that FeFe2+/Fe3+ ratios peak right at the interface. This strongly suggests the formation of a chemically distinct interface layer, which might also be magnetically distinct as indicated by the observed magnetic enhancement in the Fe2-xTixO3/alpha-Fe2O3/Al2O3 system compared to the pure alpha-Fe2O3/Al2O3 system.