Age hardening in (Ti_{1 − x}Al_x)B_{2 + Δ} thin films

MPG-Autoren

/persons/resource/persons195051

Alling, Björn
Adaptive Structural Materials (Simulation), Computational Materials Design, Max-Planck-Institut für Eisenforschung GmbH, Max Planck Society;
Department of Physics, Chemistry and Biology (IFM), Thin Film Physics Division, Linköping University, Linköping, Sweden;

Externe Ressourcen

Es sind keine externen Ressourcen hinterlegt

Volltexte (beschränkter Zugriff)

Für Ihren IP-Bereich sind aktuell keine Volltexte freigegeben.

Volltexte (frei zugänglich)

Es sind keine frei zugänglichen Volltexte in PuRe verfügbar

Ergänzendes Material (frei zugänglich)

Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar

Zitation

Mockute, A., Palisaitis, J., Alling, B., Berastegui, P., Broitman, E., Näslund, L. Å., et al. (2017). Age hardening in (Ti_{1 − x}Al_x)B_{2 + Δ} thin films. Scripta Materialia, 127, 122-126. doi:10.1016/j.scriptamat.2016.09.021.

Zitierlink: https://hdl.handle.net/21.11116/0000-0001-714A-D

Zusammenfassung

Thin films of (Ti0.71Al0.29)B2 + 1.08 have been deposited by magnetron sputtering. Post-deposition annealing at 1000 °C for 1 h results in increased hardness and elastic modulus, from 32 to 37 GPa and from 436 to 461 GPa, respectively. In both as-deposited and annealed states the films adhere well to the substrate, indicating no considerable internal stress. The initial high hardness is attributed to a columnar microstructure consisting of crystalline (Ti,Al)B2 columns separated by an amorphous B matrix. The observed age hardening corresponds to phase separation within the (Ti,Al)B2 columns including the formation of Ti-deficient crystallites within the grain interior upon annealing. © 2016 Acta Materialia Inc.