Synthesis, crystal structure and properties of RbMnO2

MPS-Authors
/persons/resource/persons280385

Pfeiffer,  S.
Abteilung Jansen, Former Departments, Max Planck Institute for Solid State Research, Max Planck Society;

/persons/resource/persons280091

Jansen,  M.
Abteilung Jansen, Former Departments, Max Planck Institute for Solid State Research, Max Planck Society;

External Resource
No external resources are shared
Fulltext (restricted access)
There are currently no full texts shared for your IP range.
Fulltext (public)
There are no public fulltexts stored in PuRe
Supplementary Material (public)
There is no public supplementary material available
Citation

Pfeiffer, S., & Jansen, M. (2007). Synthesis, crystal structure and properties of RbMnO2. Zeitschrift für anorganische und allgemeine Chemie, 633(15), 2558-2562.


Cite as: https://hdl.handle.net/21.11116/0000-000E-B4E2-7
Abstract
RbMnO2 was prepared via the azide/nitrate route. Stoichiometric mixtures of the precursers (Mn2O3, RbN3 and RbNO3) were heated in a special regime up to 600 C and annealed at this temperature for 30 h in specially designed silver crucibles. Single crystals have been grown by annealing a 1:1 mixture of Rb2O and MnOx at 585 C for 1200 h. According to the crystal structure determination Mn3+ is in a square-pyramidal coordination by oxygen. These [MnO5] units form double chains extending along the crystallographic c-axis. RbMnO2 shows Curie-Weiss behaviour down to similar to 100 K. A fit of the susceptibility data yields an average value of the magnetic moment (per manganese atom) of mu(eff) = 5.33 mu(B), and theta(P) = -820 K. At 50 K and low field strength onset of ferromagnetic order due to spin canting has been observed.