Item

Abstract

Selective acetylene hydrogenation is an important method for removing traces of acetylene in the ethylene feed for the production of polyethylene. Typical catalysts, like Pd dispersed on metal oxides are widely used for this reaction and show a limited selectivity and long-term stability. This can be attributed to the presence of active-sites ensembles on the catalyst surface. This drawback can be overcome by using the intermetallic compound PdGa which possesses palladium atoms in the crystal structure well isolated from each other by a gallium shell. PdGa shows higher selectivity and increased long-term stability compared to the commercial catalysts, including PdAg alloys. In the present work the surface of the intermetallic compound PdGa was probed by in situ XPS as well as CO adsorption using FTIR spectroscopy.
The XPS investigation before hydrogenation revealed a significant modification of the Pd electronic state in the intermetallic compound compared to Pd metal: the Pd3d5/2 peak is shifted by 1 eV to higher binding energy. In situ XPS measurements, performed at ~1 mbar pressure, showed a high stability of the Pd surface states without appearance of any additional components or significant shifts of the Pd3d5/2 peak when applying the reactive atmosphere and temperature (1.0 mbar of H2 + 0.1 mbar of C2H2 at 120 ºC). This is in contrast to Pd metal for which the formation of an additional Pd component during alkyne hydrogenation was detected. Investigation of carbon and palladium depth profiles for PdGa indicates the absence of a subsurface carbon-containing phase, distinguishing this material decidedly from metallic palladium catalysts.
The adsorption of CO on the PdGa compound at room temperature results in the appearance of only one band with a maximum at 2047 cm-1, which corresponds to linear Pd–CO carbonyls. It should be mentioned that the observed band (2047 cm–1) is shifted to lower wavenumbers compared to the respective CO (on-top) species forming upon adsorption on metallic palladium (2100-2080 cm–1), which is an indication for the modification of the Pd electronic states by covalent bonding in the investigated intermetallic compound. The absence of bands due to bridged carbonyls in the observed spectra and the fact that the observed band is not coverage dependent indicated that the active sites in PdGa are really isolated.
Characterization of PdGa by FTIR and in situ XPS revealed high surface stability during the reaction of acetylene hydrogenation and confirms the isolation of the active Pd site on the surface. In combination with modified electronic Pd states due to covalent bonding in the intermetallic compound it leads to superior catalytic properties like high selectivity and long-term stability during the partial hydrogenation of acetylene.