The three-dimensional equilibrium crystal shape of Pb: Recent results of theory and experiment

MPS-Authors
/persons/resource/persons22273

Yu,  Dengke
Theory, Fritz Haber Institute, Max Planck Society;

/persons/resource/persons22064

Scheffler,  Matthias
Theory, Fritz Haber Institute, Max Planck Society;

External Resource
There are no locators available
Fulltext (restricted access)
There are currently no full texts shared for your IP range.
フルテキスト (公開)

APA-87-391-2007.pdf
(全文テキスト(全般)), 328KB

付随資料 (公開)
There is no public supplementary material available
引用

Bonzel, H. P., Yu, D., & Scheffler, M. (2007). The three-dimensional equilibrium crystal shape of Pb: Recent results of theory and experiment. Applied Physics A, 87(3), 391-397. doi:10.1007/s00339-007-3951-7.


引用: https://hdl.handle.net/11858/00-001M-0000-0011-0176-8
要旨
The three-dimensional equilibrium crystal shape (ECS)is constructed from a set of 35 orientation-dependent surface energies of fcc Pb which are calculated by density functional theory in the local-density approximation and distributed over the [110] and [001] zones of the stereographic triangle. Surface relaxation has a pronounced influence on the equilibrium shape. The (111), (100), (110), (211), (221), (411), (665), (15,1,1), (410) and (320) facets are present after relaxation of all considered surfaces, while only the low-index facets (111), (100) and (110) exist for the unrelaxed ECS. The result for the relaxed Pb crystal state is in support of the experimental ECS of Pb at 320-350 K. On the other hand, approximating the surface energies of vicinal surfaces by assuming a linear relationship between the Pb(111) first-principles surface energy and the number of broken bonds of surface atoms leads to a trivial ECS that shows only (111) and (100) facets, with a 6-fold symmetric (111) facet instead of the correct 3-fold symmetry. It is concluded that the broken bond rule in this simple linear form is not a suitable approximation for obtaining the proper three-dimensional ECS and correct step formation energies.