Ru nanoparticles stabilized by organosilane fragments: Influence of the initial Si/Ru ratio and thermal stability

MPS-Authors
/persons/resource/persons21948

Pelzer,  Katrin
Inorganic Chemistry, Fritz Haber Institute, Max Planck Society;

External Ressource
No external resources are shared
Fulltext (public)
Supplementary Material (public)
There is no public supplementary material available
Citation

Pelzer, K., Candy, J.-P., & Basset, J.-M. (2006). Ru nanoparticles stabilized by organosilane fragments: Influence of the initial Si/Ru ratio and thermal stability. Poster presented at ISSPIC 13, Goteborg, Sweden.


Cite as: http://hdl.handle.net/11858/00-001M-0000-0011-03DF-C
Abstract
The decomposition of the organometallic ruthenium precursor [Ru(COD)(COT)] (COD: 1,5-cyclooctadiene; COT: 1,3,5-cyclooctatriene) in mild conditions (20 ◦C, 3 bar H2) in n-pentane leads, in the presence of octylsilane (H3 SiC8H17) to the formation of stable Ru nanoparticles with narrow size distribution. The solids obtained after washing and drying were fully characterized by elemental analysis, TEM with EDX, infra red measurements as well as solid state 13C CP-MAS NMR investigations. The influence of the initial octylsilane/Ru(COD)(COT) ratio ranging from 0.2 to 2.0 was studied. It was observed that the size of the nanoparticles decreases with the initial Si/Ru ratio. The thermal stability of these nanoparticles (Si/Ru = 1) was also studied and as expected the size of the particles drastically increases after treatment under H2 at 500 ◦C, while surprisingly under neutral atmosphere, there is only a slight increase.