Depth profiling of a CdS buffer layer on CuInS₂ measured with X-ray photoelectron spectroscopy during removal by HCl etching

MPG-Autoren

/persons/resource/persons36557

Johnson, Benjamin
Inorganic Chemistry, Fritz Haber Institute, Max Planck Society;

Externe Ressourcen

Es sind keine externen Ressourcen hinterlegt

Volltexte (beschränkter Zugriff)

Für Ihren IP-Bereich sind aktuell keine Volltexte freigegeben.

Volltexte (frei zugänglich)

HCl Etch Final.pdf
(beliebiger Volltext), 295KB

Ergänzendes Material (frei zugänglich)

Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar

Zitation

Johnson, B., Klaer, J., Fischer, C.-H., & Lauermann, I. (2012). Depth profiling of a CdS buffer layer on CuInS₂ measured with X-ray photoelectron spectroscopy during removal by HCl etching. Thin solid films, 520(7), 2829-2832. doi:10.1016/j.tsf.2011.10.144.

Zitierlink: https://hdl.handle.net/11858/00-001M-0000-0010-1EC8-1

Zusammenfassung

A ~ 35 nm thick CdS buffer layer has been wet-chemically deposited on a CuInS2 thin layer solar cell absorber and subsequently removed through a stepwise HCl etch process. Sequential etching times of two and three seconds were initially performed to gradually remove the CdS top-layer and leave the CuInS2 surface intact. After each step an investigation of the sample with X-ray photoelectron spectroscopy was used to determine the stoichiometry and elemental binding energies of the sample surface. After the removal of the CdS layer longer etching times were used to study the long-term effects of the HCl. The resulting depth profile revealed Cu diffusion from the CuInS2 into the CdS, although the Cu atoms did not reach the surface of the buffer layer. In addition, a Cd containing layer was left on the sample surface after more than six hours of etching time and is apparently insoluble in HCl, showing that the Cd-S bonds in this layer differ from those in CdS. This method can also be used with other top-layers to create depth profiles.